It is possible and likely, however, that even if grain boundary melting did not occur, substantial penetration by a solid state diffusion mechanism would have occurred as evidenced by the high concentration of sulfides in the grain interiors near the oxide layer.
Tra l'altro si trovano grafici molti simili a quelli visti nell'analisi effettuata sui 4 campioni.
...allora, concludeva così:
The severe corrosion and subsequent erosion of Samples 1 and 2 are a very unusual event. No clear explanation for the source of the sulfur has been identified. The rate of corrosion is also unknown. It is possible that this is the result of long-term heating in the ground following the collapse of the buildings. It is also possible that the phenomenon started prior to collapse and accelerated the weakening of the steel structure. A detailed study into the mechanisms of this phenomenon is needed to determine what risk, if any, is presented to existing steel structures exposed to severe and long-burning fires.
_________________
“Se un ebreo ortodosso mi considera "immondo" o mi saluta per primo per non dover essere costretto a rispondere al mio saluto, la cosa non preoccupa più di tanto.” (John) 9/11 anomalies
Non puoi inviare messaggi. Puoi vedere le discussioni. Non puoi rispondere. Non puoi modificare. Non puoi cancellare. Non puoi aggiungere sondaggi. Non puoi votare. Non puoi allegare files. Non puoi inviare messaggi senza approvazione.